02 — Product Portfolio
The Portfolio
Nine architectural glass families — specified, sourced and inspected to international standard. Every family is available tempered, laminated or as an insulated unit where the specification requires it.
- AssemblyAssembly: Outer lite — Tempered or laminated; Low-E coating — Solar and thermal control; Cavity — Argon or krypton fill; Spacer — Thermoplastic, desiccant filled; Inner lite — Dual-seal edge: butyl / polysulfide.
- AssemblyAssembly: Compression zone — >69 MPa surface (EN 12150); Tensile core — 120–200 MPa bending strength; Compression zone — Granular break pattern.
- AssemblyAssembly: Outer lite — 3–10 mm; Interlayer — PVB or SGP, 0.38–1.52 mm; Inner lite — 3–10 mm · STC 34–52.
- AssemblyAssembly: Ceramic frit — Screen printed pattern; Fusion — Fired into the surface at 620–680 °C; Substrate — Tempered lite, 4–19 mm.
- AssemblyAssembly: Tempered lite — Loaded to the chamber; Soak cycle — 290 °C ± 10 °C, EN 14179-1; Hold — Minimum 2 hours at temperature; Released batch — <0.1% residual breakage.
- AssemblyAssembly: Panel — Up to 16,000 × 3,300 mm; Section — 15–200 mm thickness; Build-up — Tempered, laminated or insulated.
- AssemblyAssembly: Outer lite — Bent to project radius; Interlayer or cavity — Per specified build-up; Inner lite — Formed to matching template.
- AssemblyAssembly: Relief face — Three-dimensional kiln-formed surface; Body — 10–50 mm section; Mould face — Custom refractory mould, above 800 °C.
- AssemblyAssembly: Rolled face — Engraved roller texture; Substrate — Clear or low-iron, 3–8 mm; Processing — Tempered, laminated or in an IGU.
Nine material familiesTechnical data summary
Publication 01
Definitive document
The complete Architectural Glass Portfolio
Thirty pages covering the nine glass families, technical data, project references, certifications and the full trading and project service.
Download the portfolio — PDF · 21 MB · 30 pages